英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha

英语翻译XRD and XPS.The X-ray powder diffraction patternsof the AgI/BiOI composites with different AgI amounts areshown in Figure 1.It is observed that all the peaks of the pureBiOI sample (Figure 1a) coincide with the standard tetragonalBiOI pha 哪里有做XRD和XPS实验? 外文翻译,求高人帮忙翻译一下!急!谢谢!The thermal behaviour of TiO2-WO3-V2O5 catalysts with various vanadia contents (1, 2 and 3 wt.% V2O5) was investigatedusing X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spe 哪里可以做xrd测试和xps测试,急求xrd和xps测试! 纤维测XRD和XPS如何制样 英语翻译Abstract：The properties of the passive film formed on 2205 stainless stee1 in acetic acid at high temperature that contained chlorideions were studied by atomic absorption spectrometry(AAS),X—ray photoelectron spectroscopy(XPS),and el XPS & XRD 能测出物质什么信息,怎么分析测出来的图谱呢? 英语翻译6 ConclusionBased upon hardness testing,XRD analysis and microstructural characterization of the weld overlay surfacing,the following can be concluded:(1) Hardfacing is the most versatile process to improve the life of the worn out compon 英语翻译句子如下：An artifact of the sample preparation for XPS analysis was considered,but various procedures gave the same result.重点在前半句,XPS为专有名词--X射线光电子能谱求英化达人翻译 哪里有做XRD和XPS实验ITO导电薄膜做XRD和XPS实验,请问南京哪里可以做还有ITO导电薄膜金相实验,最好可以一起做,谢谢! TEM,EDS ,SEM,FE-SEM,STM,AFM,XRD,XPS,FT-IR,UV-VISQ全称和中文名称是什么呀? 英语翻译The X-ray diffraction (XRD) patterns were recordedon a X-ray power diffractometer using Cu Ka radiation(0.15418 nm) (PANalytical Co.X’pert PRO,Netherlands) operated under a voltage of 40 kV and acurrent of 40 mA. 英语翻译3.Results anddiscussion3.1.Kineticsof PU,XPS and EPS degradationThe TG and DTGresults of PU,XPS and EPS under various heating rates (5,10,15,20 ◦C/min)in a nitrogen environment are presented in Figs.1–3,respectively.There are many 英语翻译During thethermal degradation of XPS,the activation energy increases before a= 0.25 andthen the value stabilizes in the range of 220–230 kJ·mol−1.Through theentire process,the E values of XPS are always smaller than that of EPS a 英语翻译4.ConclusionA sol–gel,spray-drying method was used to prepareLiMn2O4 powder.Via DTA,TGA,IR,XRD and SEManalysis,it was shown that the structure and morphologyof LiMn2O4 powder were strongly affected by thespray speed and the heat treatme 英语翻译如题：the significance of changes in the structure is decreasing with the total amount of foreign oxides in the sample.the changes in XRD pattern and lattice parameters that are induced by Fe2O3 decrease with the total amount of doped 英语翻译As per Atamert and Bhadeshia [19] Si is ferrite stabilizer,it retains Cr in the matrix.However in XRD research Cr is precipitated in presence of high amount of Si.This is contradictory to results of Atamert and Bhadeshia.The reason may be 英语翻译the ( ) ( ) ( ) and ( ) ( ) ( )