The waveforms of the currents are shown in Fig.5.Here,all waveforms were plotted from the raw data without filtering.In this experiment,the melting current (or total current) is approximately 225amps while the base metal is approximately 80amps.There are no spatters observed although the base metal current is only 80amps and is not pulsed.(Conventional GMAW would require a 225amps or greater continuous base metal current for 1.2mm diameter steel wire to produce the spray transfer which can eliminate spatters.) It is apparent that the Dual Bypass GMAW method as tested on steel plates is feasible.
The ultimate goal of this research is to provide a new process to weld the LANL’s aluminum rings with a minimal heat input without significantly compromising the productivity.The ring contains a groove which requires machining to produce.In this present study,aluminum cylinders with 0.32mm (0.125 inch) wall thickness and 16.5mm (6.5 inch) OD are used to conduct experiments for process and welding procedure developments before actual rings are joined.

英语翻译The waveforms of the currents are shown in Fig.5.Here,all waveforms were plotted from the raw data without filtering.In this experiment,the melting current (or total current) is approximately 225amps while the base metal is approximately
波形海流图所示.5.在这里,所有波形绘制了从原始数据过滤.在这个实验中,融化电流（或总电流）大约是二二五安培而贱金属大约是八十○安培.没有飞溅指出尽管贱金属目前只有八零安培,而不是脉冲.（常规气体保护焊,就需要更大的持续二二五安培或基本金属当前的一点二毫米直径钢丝生产喷雾转让,可以消除飞溅.）这是明显的双重绕道气体保护焊方法测试钢板是可行的.
最终目标,本研究提供一个新的进程的洛杉矶国家实验室的焊接铝环最小热输入大大损害生产力.环包含槽要求加工生产.在本研究,铝气瓶0.32毫米（ 0.125英寸）壁厚和十六点五毫米（ 6.5英寸）的OD是用来进行实验的过程和焊接工艺的发展实际环前加入.